The reactive Al/Fe₂O₃/PTFE material was prepared by molding and sintering method. The quasi-static compression feature and impact sensitivity of Al/Fe₂O₃/PTFE material molded in different proportioning and at different sintering temperature were comparatively tested by universal testing machine, drop hammer machine and high-speed photography instrument. Its ignition performance was analyzed. Results show that: specimens with 60% and 70% polytetrafluoroethylene(refer to as PTFE) sintering at 330 ℃ have the highest strength and the maximum real stress is 46 MPa. Specimens with 40% PTFE sintering at 350 ℃ have the highest impact sensitivity, and its characteristic drop height H₅₀ is 95 cm. The Al/Fe₂O₃/PTFE material under the impact ignition conditions will appear the high temperature metal slag jet phenomenon. The research results have raised the understanding of the deformation behavior and impact reaction of Al/Fe₂O₃/PTFE material, which has laid a good foundation for the following research.