Marcela Jungová , Svatopluk Zeman , Adéla Husarová
2011, 19(6):603-606. DOI: 10.3969/j.issn.1006-9941.2011.06.001
摘要:Fractions of β-HMX (β-1,3,5,7-tetranitro-1,3,5,7-tetrazocane) have been used to demonstrate the mutual relationship between friction and impact sensitivities. Inclusion of an additional twelve nitramines into this scenario resulted in a series of partial relationships, which were determined from the molecular structure of these substances. It was also found that there is a relation between increasing heats of fusion of the nitramines studied and their decreasing friction sensitivities. Comparison of friction sensitivity with heats of fusion, ΔHm,tr of the studied nitramines shows that the increase in ΔHm,tr values is more or less connected with a decrease in friction sensitivity.
Marcela Jungová , Svatopluk Zeman , Adéla Husarová
2011, 19(6):607-609. DOI: 10.3969/j.issn.1006-9941.2011.06.002
摘要:The friction sensitivity (FS) of five linear and eight cyclic nitramines has been determined. Arrhenius parameters of non-autocatalyzed thermal decomposition of these nitramines were used for comparison of the FS values with thermal reactivity. Generally, increasing values of activation energies of non-autocatalyzed decomposition of the studied nitramines are connected with decreasing FS values. A similar trend was found in the relation between FS and hypothetical initiation temperature for 5% conversion of the nitramines after 50 μs of their thermolysis, however, if in the given series of nitramines their initiation reactivity is predominantly determined by the energy content of their molecules and closer similarity of their molecular structures, then the above-mentioned trend may be opposite. The found relationships were used for prediction and verification of the activation energy of non-autocatalyzed thermal decomposition of 2,5-dinitro-2,5-diazahexane.
Svatopluk Zeman , Marcela Jungová , Adéla Husarová
2011, 19(6):610-612. DOI: 10.3969/j.issn.1006-9941.2011.06.003
摘要:The friction sensitivities (FS) of five linear and eight cyclic nitramines have been determined. These FS values were compared with the respective detonation velocities,D, and with the dimensionless ratio created by relating the heat of explosion,Qreal, to the activation energy,Ea, of non-autocatalyzed thermal decomposition of the explosives concerned. For the nitramaines studied, these comparisons show a general trend of FSdecreasing with increasing energy content.
Zdeněk Friedl , Marcela Jungová , Svatopluk Zeman , Adéla Husarová
2011, 19(6):613-615. DOI: 10.3969/j.issn.1006-9941.2011.06.004
摘要:The friction sensitivity (FS) of five aliphatic linear and eight cyclic nitramines has been determined and correlated with DFT B3LYP/6-31-G(d,p) // 6-311+G(d,p) positive (VS,max) and negative (VS,min) extremes of molecular surface electrostatic potentials VS(r). While there is an ambiguous relationship between the VS,max values and FS values, the decrease of FS is connected (more or less) with increase in VS,min values.
2011, 19(6):616-620. DOI: 10.3969/j.issn.1006-9941.2011.06.005
摘要:应用电性拓扑状态(Electrotopological State,E-state)指数模拟分析了16种硝胺类化合物和34种硝基芳烃化合物的静电感度。用多元线性回归的方法对两组物质建立定量结构-性质相关(QSPR)模型,硝胺类化合物模型的相关系数和标准偏差分别为0.782和0.217,硝基芳烃化合物模型的相关系数和标准偏差分别为0.717和0.195。模型分析表明:原子类型电性拓扑状态指数与硝基类含能材料静电感度有较好的相关性,可有效对硝基类含能材料静电感度进行预测; 同时,电性效应是影响静电感度的重要因素。
2011, 19(6):621-626. DOI: 10.3969/j.issn.1006-9941.2011.06.006
摘要:采用折光指数匹配的光学显微技术、浮沉分析技术、扫描电镜、激光粒度等分别对比研究了高品质RDX(D-RDX)与普通RDX的晶间包藏物、晶体表观密度、表面光滑度、颗粒粒度与粒度跨度、晶体形状等晶体特性。结果表明: D-RDX内部缺陷和杂质很少,表观密度大于1.7980 g·cm-3, 普通RDX内部存在较多孔隙和杂质,表观密度小于1.7930 g·cm-3,D-RDX比普通RDX表面更光滑,粒度分布更窄。用D-RDX代替普通RDX与TNT浇铸,当D-RDX含量从60%提高到70%时,颗粒间的孔隙率增加0.66%,药柱的冲击波感度从隔板厚度17 mm增加到18 mm,但仍然低于普通RDX的冲击波感度(20 mm),D-RDX冲击波感度比普通RDX降低10%~15%; 将D-RDX和普通RDX用于浇铸固化PBX配方,D-RDX的冲击波感度比普通RDX降低31.4%。研究表明,D-RDX和普通RDX晶体特性的不同导致其冲击波感度的显著差异。
2011, 19(6):627-631. DOI: 10.3969/j.issn.1006-9941.2011.06.007
摘要:采用撞击感度、摩擦感度和热分解特性测试方法,研究了二茂铁种类对超细AP/二茂铁体系感度的影响。结果表明,本研究所涉及的二茂铁衍生物均使超细AP/二茂铁催化剂混合物的撞击感度和摩擦感度显著升高; 超细AP/二茂铁催化剂体系的撞击感度与二茂铁催化剂的铁含量不存在相关关系,而超细AP/二茂铁催化剂体系的摩擦感度与二茂铁催化剂的铁含量存在正相关关系; 某些二茂铁催化剂(SH-F-1、SH-F-2、SH-F-3、GFP、SH-F-5)/超细AP体系的DSC曲线中AP的晶型转变峰之前出现新的放热峰,表明其热感度较大。
徐容 , 李洪珍 , 康彬 , 李金山 , 黄明 , 卢校军
2011, 19(6):632-636. DOI: 10.3969/j.issn.1006-9941.2011.06.008
摘要:采用标准隔板试验方法分别研究了HMX的晶体内部空隙(用晶体表观密度表征)、颗粒度、形貌和缺陷类型对冲击波感度的影响规律。冲击波感度测试采用隔板试验,药柱配方为HMX/食用油 (76/24),药柱采用液体填充方式制备。隔板试验研究表明: 随着非孪晶HMX晶体表观密度在1.8992~1.9016 g·cm-3范围内增加,炸药配方的冲击波感度降低,隔板厚度从15.5 mm降到13.2 mm,晶体内部空隙率与隔板厚度基本成线性关系; 当晶体表观密度基本相近时,在20~650 μm粒度范围内,随着颗粒度的增加,非孪晶HMX炸药配方的冲击波感度增加,隔板厚度从13.0 mm 升到14.3 mm; 无论是粗颗粒还是细颗粒,含有孪晶缺陷HMX的冲击波感度显著高于非孪晶HMX; 当晶体表观密度和颗粒尺寸相近时,晶体颗粒的外观形貌对炸药冲击波感度影响不大。
2011, 19(6):637-640. DOI: 10.3969/j.issn.1006-9941.2011.06.009
摘要:α′、β、γ晶型的三氢化铝(AlH3)是乙醚法合成α-AlH3的常见伴生晶型,它们会影响α-AlH3的热力学稳定性和安全性。在常温存储条件,经历约650 d后,γ晶型使得AlH3的分解率由2.13%上升到5.15%。通过撞击、摩擦、静电火花感度测试,含有其他晶型的α-AlH3比纯净α-AlH3的摩擦感度和静电火花感度均有不同程度的增加,其中对静电感度影响较大,与晶型较好的α晶型AlH3相比其E50数值相差约5-10倍。
2011, 19(6):641-645. DOI: 10.3969/j.issn.1006-9941.2011.06.010
摘要:采用B3LYP/6-311G*方法对三叠氮化铝进行结构优化;理论计算了其密度、升华焓、生成焓,将其作为单质炸药,计算了其爆炸参数,并与TNT作比较;再将其加入硝酸铵与梯恩梯的混合炸药中,按零氧平衡原则预测混合炸药各爆炸参数,并与含有相同质量分数Al的混合炸药作比较。结果表明: 三叠氮化铝的爆热、爆容、爆温、爆速、爆压、作功能力分别为5170.20 kJ·kg-1、585.62 L·kg-1、5028.12 K、9095.23 m·s-1、31.02 GPa、1105.14 kJ·kg-1,除爆容小于TNT及作功能力与TNT相当外,其余性能都优于TNT,因此是一种潜在的单质炸药;铝含量为6%时,三叠氮化铝、硝酸铵和梯恩梯混合炸药以上各参数分别为4351.49 kJ·kg-1、892.22 L·kg-1、3142.50 K、8344.09 m·s-1、27.55 GPa、1417.11 kJ·kg-1; 三叠氮化铝能提高硝酸铵与梯恩梯混合炸药的爆热、爆温、爆速、爆压和作功能力,是一种潜在的高能可燃剂。
2011, 19(6):646-649. DOI: 10.3969/j.issn.1006-9941.2011.06.011
摘要:用差示扫描量热仪,在四种升温速率下,测定了KNO3/C=65/30,KNO3/C=75/15两种组分配比的无硫型黑火药的DSC曲线,并与普通黑火药的热分解数据与热行为进行了对比。在实验结果对比分析的基础上,运用Kissinger、Ozawa和Satava-Sesták方程求解了黑火药发生热分解时的活化能和指前因子。结果表明: 无硫黑火药与普通黑火药相比,起始分解温度降低,放热值降低,其中含碳量较低的黑火药,无硫黑火药活化能升高,机械感度也较低。
刘芮 , 尹艳丽 , 张同来 , 杨利 , 张建国 , 周遵宁 , 乔小晶 , 王文杰 , 王丽琼
2011, 19(6):650-655. DOI: 10.3969/j.issn.1006-9941.2011.06.012
摘要:采用动态真空安定性试验(DVST)方法研究了奥克托今(HMX)的热分解过程,利用普适积分法和微分方程法得到了HMX热分解反应的活化能和指前因子。结果表明,不同恒温温度下HMX的热分解机理函数不同。在100~110 ℃范围内,HMX的热分解过程遵循三维扩散机理的Ginstling-Brounstein方程; 在120~140 ℃范围内,遵循一维扩散机理的抛物线方程; 150 ℃时遵循二维扩散机理的Valensi方程。HMX热分解反应速率常数k随温度的升高而增大,但不符合Van′t Hoff规则。HMX在150 ℃以下放气量均小于2.0 mL·g-1,表明HMX具有良好的热安定性。对HMX进行高温加速老化试验,以分解深度为0.1%所需时间(tT)与温度(T)的关系数据拟合Semenov方程为:lntT=12157.95/T-19.0052,据此预估25 ℃下HMX的储存寿命为90.6 a。
刘颖 , 杨茜 , 陈利平 , 何中其 , 陆燕 , 陈网桦
2011, 19(6):656-660. DOI: 10.3969/j.issn.1006-9941.2011.06.013
摘要:对现有的固体含能材料热感度表征方法进行了简述,并针对现有表征方法无法适用于液态含能材料热感度测试的局限性,提出了采用绝热加速量热仪(ARC)表征含能材料热感度的方法。用ARC测试了4种固体含能材料太安(PETN)、黑索今(RDX)、奥克托今(HMX)、梯恩梯(TNT)以及2种液态含能材料硝基乙烷(NE)、硝酸异辛酯(EHN)的绝热分解过程,根据所得热动力学数据计算得出了这些被测试样不同爆炸延滞期对应的爆发点。就4种固体含能材料而言,ARC测试得到的热感度排序为PETN>RDX>HMX>TNT,此结果与传统的伍德合金浴法的测试结论一致,认为ARC可以应用于固体及液态含能材料的热感度测试。6种被测试样的热感度排序为EHN>PETN>RDX>HMX>TNT>NE。
2011, 19(6):661-663. DOI: 10.3969/j.issn.1006-9941.2011.06.014
摘要:采用自主研制的化学反应性试验在线检测系统,对HMX基高聚物粘结炸药试件的热安全性及与接触材料(硅泡沫垫层和聚氨酯粘接胶)的相容性进行了研究。结果表明,HMX基高聚物粘结炸药试件有较好的热稳定性。100 ℃下受热1.15个月的CO2和N2O的逸出量达0.1 mL·g-1。与HMX基高聚物粘结炸药试件相比,HMX基高聚物粘结炸药与硅泡沫垫层或聚氨酯粘接胶混合物的N2O的释出量稍有增加,但净增量较小,显示HMX基高聚物粘结炸药试件与两种接触材料是相容的。
2011, 19(6):664-668. DOI: 10.3969/j.issn.1006-9941.2011.06.015
摘要:为了模拟爆炸箔起爆器中HNS药柱在热烤环境下的热响应状态,设计了密封的样品试管,并对Φ3 mm×4 mm、Φ4 mm×5 mm和Φ4 mm×6 mm 3种尺寸,装药密度为90% TMD的HNS药柱进行了3.3 ℃·h-1、5 ℃·min-1和10 ℃·min-1条件下的热烤试验。通过试验后样品试管及其薄弱环节的破坏和变形程度、钢凹深度来判定反应的剧烈程度,并与非密封状态下的试验结果进行了对比。研究结果表明,密封状态下,HNS药柱的反应比非密封药柱的剧烈。密封状态HNS药柱发生反应的环境温度(302.5~314.7 ℃)明显低于非密封药柱的温度(328~335 ℃)。在5 ℃·min-1或10 ℃·min-1的试验条件下,密封HNS药柱的起始反应温度随着装药量的增大而降低,大装药量的结构更容易形成热积累,对热更为敏感。
赵孝彬 , 李军 , 程立国 , 王宁 , 王拯 , 陈中娥 , 王晨雪 , 秦超 , 程新丽
2011, 19(6):669-672. DOI: 10.3969/j.issn.1006-9941.2011.06.016
摘要:以HTPE推进剂、GAP推进剂为对象,采用慢速烤燃试验装置结合热电偶测温及传感器测压技术,研究了固体推进剂慢速烤燃特性的影响因素,包括配方组成、燃速、升温速率、约束条件、自由体积等。HTPE推进剂具有优异的慢速烤燃特性,10% HMX的加入使其慢速烤燃的响应程度增加,自由体积对其慢速烤燃的响应程度没有明显影响;燃速从10.1 mm·s-1增加到32.2 mm·s-1,升温速率从3.3 ℃·h-1增加到1 ℃·min-1,对GAP推进剂慢速烤燃的响应程度影响较小;增加夹板约束后,HTPE推进剂和GAP推进剂慢速烤燃的响应程度增加。
2011, 19(6):673-678. DOI: 10.3969/j.issn.1006-9941.2011.06.017
摘要:为了解老化对PBX-6炸药件安全性的影响,分别开展了温度75 ℃、100 d和65 ℃、180 d的加速老化试验。对加速老化前后的炸药件,进行了热爆炸试验、火烧试验和跌落试验,对比分析了试验数据,结果表明,老化炸药柱的热爆炸延滞期缩短,热安全性降低;老化炸药件的烤燃时间缩短,烤燃温度降低,爆燃后对炸药外壳的破坏程度更大,热安全性下降;老化炸药件跌落爆燃时产生的冲击波超压大,靶板上未反应的剩余药量少,撞击安全性降低。
2011, 19(6):679-683. DOI: 10.3969/j.issn.1006-9941.2011.06.018
摘要:概述并分析了Arrhenius、时间温度叠加原理和神经网络三种高聚物粘结炸药(PBX)老化模型的建立方法,利用上述方法对HMX基PBX在45~75 ℃下老化后的质量变化数据建模并预测寿命。上述三种方法预测该炸药在20 ℃下质量损失0.1%的贮存寿命分别为390 a、490 a和15.2 a。三种方法预测该炸药在50 ℃和60 ℃下质量损失0.2%所需的时间分别为1127 d,182 d; 1180 d,196 d; 1375 d,220 d; 表明Arrhenius和时温叠加原理建模预测结果彼此吻合较好,而神经网络模型对低于建模温度时寿命预测可信度较低。
2011, 19(6):684-688. DOI: 10.3969/j.issn.1006-9941.2011.06.019
摘要:合理选择输入杆、输出杆长度和合适的应变片贴片位置,以实现拉伸应力波。利用PBX压缩强度远大于拉伸强度的性质,不采用承压环,在反射式霍普金森拉杆(SHTB)上对采用与铝杆端面粘接的PBX动态拉伸样品进行动态拉伸性能测试。结果显示,TATB基炸药的动态拉伸强度,在30 s-1应变率下动态拉伸强度达到了13 MPa,远高于准静态下的拉伸强度7 MPa。采用扫描电镜对样品细微破坏形貌进行了观察,结果表明,由于动静态下裂纹不同发展方式和动态下温升使粘结剂发生了软化,准静态下的拉伸破坏模式和动态下的模式明显不同,准静态下是沿晶断裂和穿晶断裂共存,动态拉伸下属于粘结剂脱粘破坏。
陈晓明 , 金鹏刚 , 张衡 , 刘来东 , 宋长文 , 张邹邹 , 赵瑛
2011, 19(6):689-692. DOI: 10.3969/j.issn.1006-9941.2011.06.020
摘要:采用隔板试验方法对发射药冲击波感度进行了系统试验,其中包括单基、双基、三基和叠氮硝胺等不同结构的发射药,以及球形、6/7和17/19的不同药型的发射药。通过冲击波感度的试验,研究了发射药冲击波感度的响应特性,得到了发射药冲击波感度的影响因素和响应规律,主要表现为,添加黑索今(RDX)、硝化甘油(NG)、叠氮硝胺(DA)等高能组分后,发射药冲击波感度增加;随着高能组分含量的增加,其冲击波感度也增加。不同的含能组分对冲击波的影响程度不同。发射药药型尺寸变大,其装填密度降低,会显著降低发射药的冲击波感度,装填密度增加10%,冲击波感度隔板值大约增加1倍。提出了发射药组份对冲击波感度贡献的定量计算的概念,可以进行发射药冲击波感度的预估。
2011, 19(6):693-696. DOI: 10.3969/j.issn.1006-9941.2011.06.021
摘要:为了估算叠氮硝胺(DIANP)的安全性能参数,进行了热刺激和机械刺激试验,获得了DIANP在不同刺激下的响应特性; 同时,为了确定生产工房的安全等级,在不同冲击波超压处进行了TNT当量测定。试验结果表明: DIANP在电引火头点燃下不燃烧、无火焰感度; DIANP的自发火温度为226 ℃; 克南试验中DIANP的极限孔径为20.0 mm; 按改进后国军标方法试验得到DIANP撞击感度爆炸百分数为75%,摩擦感度爆炸百分数为26%; 在0.3~0.02 MPa冲击波超压峰值范围内,DIANP的TNT当量为0.4~0.6。
陈朗 , 王飞 , 伍俊英 , 王晨 , 鲁峰 , 黄毅民 , 代晓淦 , 文玉史
2011, 19(6):697-704. DOI: 10.3969/j.issn.1006-9941.2011.06.022
摘要:为了给高密度炸药装药的安全性分析提供更准确的依据,在不同约束条件下(DDT管长420 mm,壁厚分别为10,20 mm),进行了PBXC03压装炸药燃烧转爆轰实验,采用电离探针测量了炸药中反应波速度,通过观测管体和反应波速度变化,判断炸药燃烧转爆轰(DDT)的情况。根据高密度炸药状态,建立了炸药燃烧转爆轰计算模型,采用燃烧反应速率方程,描述炸药反应过程。应用网格分离和节点随机失效方法计算高温高压炸药反应产物作用下管体的膨胀和破裂,考虑气体产物泄漏,压力下降对炸药反应的影响。对不同约束条件下(DDT管长420 mm,壁厚分别为5,10,20,30 mm)炸药燃烧转爆轰过程进行了数值模拟计算。结果表明: PBXC03压装炸药只有在强约束下(壁厚30 mm)才能够发生燃烧转爆轰,弱约束下(壁厚5 mm)管体破坏引起气体泄漏和压力降低是限制炸药燃烧转爆轰的主要原因。
2011, 19(6):705-708. DOI: 10.3969/j.issn.1006-9941.2011.06.023
摘要:为了研究装药密度对撞击安全性的影响,针对A-Ⅸ-Ⅱ炸药、B炸药、HMX基含铝炸药压制了不同密度的药柱。用A-Ⅸ-Ⅱ炸药压制了径向呈一定密度分布的药柱,利用400 kg落锤进行了撞击加载试验。结果显示,随着密度的增大,A-Ⅸ-Ⅱ炸药、B炸药、HMX基含铝炸药的起爆阈值增加。对于A-Ⅸ-Ⅱ炸药,当装药密度达到1.680 g·cm-3以上时,起爆阈值没有明显差别。三种炸药的起爆阈值相差不大。当A-Ⅸ-Ⅱ炸药密度分布不均匀时,其起爆阈值有所下降,低于密度相对均匀的药柱。表明装药密度及密度均匀性是影响撞击安全性的两个主要因素。
2011, 19(6):709-714. DOI: 10.3969/j.issn.1006-9941.2011.06.024
摘要:尽管侵彻动力学研究有大量的研究报道,但是主要集中于弹体结构响应和侵彻能力研究,涉及侵彻体内部装药安定性的研究较少,而且没有形成系统的装药安定性理论分析方法。本文根据弹体内部装药的塑性应力-应变本构关系,首次提出了利用弹体结构与内部装药相对位移、摩擦功、热力学原理和热点理论推导的装药热安定性结构设计塑性理论分析方法。研究过程中从空穴膨胀理论出发确定侵彻弹体的响应函数,结合牛顿第二定律,采用有限差分技术获得弹体侵彻过程的轴向阻力和惯性过载。以弹体惯性过载作为装药安定性响应的输入,通过理论分析确定弹体壳体与内部装药界面热影响区内炸药温度上升情况,分析表明:内部装药过载系数、装药长度是影响装药安定性的重要因素,而且热影响区内炸药温度上升沿装药轴线呈现非线性变化。此外,如果装药直径给定,通过计算可以确定热影响区内炸药温度上升的最大值及其发生位置。理论分析结果给出了能够定量描述装药安定性结构设计的物理参数和几何参数,可以作为装药安定性结构设计的重要依据和参考。
2011, 19(6):715-719. DOI: 10.3969/j.issn.1006-9941.2011.06.025
摘要:选用单基药、双基药、太根药和硝基胍药等发射药,采用速度为(850±20) m·s-1的12.7 mm标准穿甲弹撞击样弹,研究子弹撞击机械刺激下发射药的易损性响应特性和影响因素。结果表明: 子弹撞击对发射药的易损性响应程度与发射药能量水平无明显对应关系,但与其配方组分、药型以及子弹的穿透深度有一定关系; 约束条件对发射药子弹撞击下易损性响应影响明显,发射药在强约束条件下发生燃烧甚至比燃烧更剧烈的反应,而在弱约束条件下未发生燃烧反应。
2011, 19(6):720-724. DOI: 10.3969/j.issn.1006-9941.2011.06.026
摘要:利用铅柱压缩量、铅壔扩孔值和冲击波超压与冲量等参数定量研究了推进剂残余装药对战斗部爆炸毁伤效果的影响,并探讨了影响战斗部装药/推进剂体系铅柱压缩量的因素。试验结果表明,四种推进剂的存在对战斗部装药/推进剂体系的铅柱压缩量均有不同程度的增益作用。HTPB四组元推进剂对战斗部装药/推进剂体系的铅柱压缩量和铅壔扩孔值的贡献量要高于HTPB三组元推进剂(HTPB-3),其铅壔扩孔值的增益量分别为81.4%和54%。比例距离范围为3.5~12.5 m·kg-1/3时,HTPB-3对1 kg战斗部装药PBXN/0.6 kg HTPB-3体系的超压TNT当量和冲量TNT当量分别贡献了18.7%和19.7%。
2011, 19(6):725-729. DOI: 10.3969/j.issn.1006-9941.2011.06.027
摘要:为考察螺旋压伸工艺成型的RDX-CMDB推进剂的危险性,进行了摩擦感度、撞击感度、雷管感度、隔板、燃烧转爆轰、跌落、热安定性、爆发点、慢速烤燃和静电感度等典型试验。结果表明,该推进剂从10 m高度自由跌落不燃烧,慢速烤燃在164.2 ℃发生燃烧反应,在18 mm厚有机玻璃隔板下,仍能被冲击波引爆,摩擦感度(P)为2%,撞击感度特性落高(H50)为26.3 cm,50%发火时的静电点火能量为208.46 mJ,结果表明,该推进剂热安定性良好,对机械刺激不敏感,对冲击波刺激较敏感,该推进剂的危险等级为1.1级。
2011, 19(6):730-734. DOI: 10.3969/j.issn.1006-9941.2011.06.028
摘要:为研究碾混机在混药过程中的安全性,通过分析碾混机结构,调节进料速度、刮板角度和碾混机转速来进行生产极限的试验,观察混药过程中堵料情况,测试混药后炸药爆速,分析和讨论碾混机混药过程的安全性。研究结果表明,当碾混机转速为22.8 r·min-1,进料速度为4 t·h-1,刮板角度为24°条件下,碾混机运行具有较高的安全性,混药后膨化硝铵炸药的爆速也有明显提高。
2011, 19(6):735-738. DOI: 10.3969/j.issn.1006-9941.2011.06.029
摘要:以氰基乙酸乙酯为起始原料,用一锅法先行合成了前体化合物3-氨基呋咱-4-羧酸(AFCA),产率46%。再通过NaBH4/ZnCl2还原体系和H2O2/H2SO4氧化体系先后得到了3-氨基呋咱-4-甲醇(AFMA)及3-硝基呋咱-4-甲醇(NFMA)。用SOCl2将NFMA氯化,得到3-硝基-4-氯甲基呋咱(NFCM),NFCM与甲醇钠反应,最终得到目标化合物3-硝基呋咱-4-甲醚(NFME),产率45%。采用傅里叶红外光谱(FT-IR)、高分辨质谱(HRMS)、核磁共振(NMR)和差热-热重联用(DSC-TG)等对其进行了表征,测定了其燃烧热和感度。结果表明,NFME具有-67 ℃的低熔点,且对撞击和摩擦钝感;其分解温度为169.9 ℃,燃烧热16940.8 kJ·kg-1,生成焓407.0 kJ·mol-1,均高于传统硝酸酯类增塑剂丁基硝酸基乙硝胺(Bu-NENA)、三羟甲基乙烷三硝酸酯(TMETN)、1,2,4-丁三醇三硝酸酯(BTTN)和硝化甘油(NG)。
2011, 19(6):739-742. DOI: 10.3969/j.issn.1006-9941.2011.06.030
摘要:采用溶胶-凝胶法,结合超临界CO2流体干燥技术,制备了85% RDX的Fe2O3/Al/RDX含能材料。利用扫描电子显微镜(SEM)对样品进行了表征,其粒度为50~150 nm。对比测试了样品和原料RDX撞击感度、摩擦感度,样品的特性落高比原料RDX(2.5 kg,22.5 cm,12型工具)提高27.7 cm,其爆炸百分数比原料RDX(90°,3.92 MPa,96%)降低88%。含RDX 85%的Fe2O3/Al/RDX含能材料压制成密度为1.55 g·cm-3的药柱,爆速为7185 m·s-1,是一种钝感高能的纳米复合含能材料。
2011, 19(6):745-746. DOI: 10.3969/j.issn.1006-9941.2011.06.032
摘要:采用两种不同溶剂研究RDX单晶体的生长状况,探讨了RDX单晶切割和抛光的工艺条件。结果发现:晶体生长的溶剂性质对RDX单晶体的质量和形状有很大影响,在一定条件下能获得大尺寸的RDX单晶。RDX单晶可以切割加工成具有不同厚度和不同晶面取向的单晶片,可用于RDX炸药的起爆机理和力学响应机制等基础研究。
摘要:
摘要:
摘要: