Vlasov D A , Rudchenko E A , 朱祖良 , 董海山
摘要:本文叙述了用微米和亚微米的炸药颗粒制成的薄层炸药。它们具有临界厚度薄、用药量小、爆速高、传爆可靠、起爆能力强、破坏作用小等优点。实测结果:临界厚度仅为30μm(其宽度为2mm);爆速为8030m/s(厚度为0.04~0.06mm)。
摘要:In study of polynitrocompounds it is found that a dense crystal must not necessarily be constructed from dense molecules,and the main factors affecting the crystal structure are the electronic structure of their molecules.The correlation between the value of non-bonded intramolecular contact and the magnitude of the respective intermolecular contact seems to be unusual for this kind of Compounds.Alkoxydiazene-N-oxide and 1, 1, 4, 4,-tetranitrobutanediol-2,3 derivatives were taken as examples in this study.The obtained results concluded that the intramolecular interaction can stabilize the crystal conformation,while the increase in the intermolecular contact decreases the crystal density.
摘要:本文介绍了用TNT/RDX炸药爆炸的方法合成超细金刚石粉末的初步结果。爆炸后在容器壁上收集到的黑色固体产物中金刚石含量为27~30%。经混酸处理后得到了金刚石含量超过90%的产物,XRD和电子衍射的结果表明产物为金刚石,收率为6%左右(对炸药用量计算)。透射电镜的结果表明,这种金刚石的颗粒尺寸为3~15nm。
摘要:本文介绍了NTO铅盐、铜盐和铵盐的物化性能,并探索了它们在RDX-CMDB推进剂对燃速、压力指数和能量的贡献,认为它们是一种新型含能高压平台催化剂。
摘要:本文介绍了利用粘结拉伸法和球形夹具拉伸法测定JO-9159在不同的应变速率、不同温度及不同加载历程下的拉伸应力-应变曲线,同时给出TNT/RDX(40/60)在不同横梁速度及不同温度下的拉伸应力-应变曲线。根据塑性力学理论,对所测出的各条曲线的数据通过拟合处理,导出含有一定物理意义的数学模型。
摘要:本文通过工业电雷管发火电流(I)和引燃冲量(K)的试验研究,证明了K-I关系曲线中极小值(即最小引燃冲量)的存在;补充解释了GB8031标准中引燃冲量的特定含义;提出了应确定最小引燃冲量和最大不引燃冲量指标的重要性;同时阐明了用升降法测量百毫秒发火电流(I100)过程中,发火概率(P)取值应从0.9999改为0.50的理由。
摘要:应用高速扫描摄影拍摄了表征电雷管特性的随机变量,如作用时间,得到电雷管同时起爆爆炸同步性(极差)。研究了雷管母体标准差与样本极差间的函数关系。在已知母体雷管标准差的情况下,可以确定由n个雷管组成的样本的极差不超过某一指标的概率;或在样本的极差不超过某一指标概率的条件下,可以确定母体的标准差。这在科研生产和使用中具有重要的应用价值。本方法的测量误差小于或等于0.03μs。