Preparation and Thermal Properties of Fine LLM-105 with Different Crystal Form

Author:

Affiliation:

Xi’an Modern Chemistry Research Institute,Xi’an Modern Chemistry Research Institute, Xi’an 710065, China,Xi’an Modern Chemistry Research Institute, Xi’an 710065, China,Xi’an Modern Chemistry Research Institute, Xi’an 710065, China,Xi’an Modern Chemistry Research Institute, Xi’an 710065, China,Xi’an Modern Chemistry Research Institute, Xi’an 710065, China

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

摘要:

采用溶剂-非溶剂重结晶技术制备了类球形和立方体结构两种不同晶形的细颗粒2,6-二氨基-3,5-二硝基吡嗪-1-氧化物（LLM-105），重均平均粒径D₅₀分别为2.750 μm和6.206 μm，撞击感度为35.5 cm和 34.7 cm。采用热重-微商热重（TG-DTG）和差示扫描量热法（DSC）对LLM-105进行了热分析，根据Kissinger方程计算了LLM-105的热分解动力学参数，其热分解活化能为257.55 kJ·mol^-1，指前因子为3.3×10¹⁹s^-1，线性相关系数为0.9930。

Abstract:

Two kinds of resemble sphere and cubic crystals of 2,6-diamino-3,5-dinitropyrazine-1-oxide(LLM-105) were prepared using solvent-nonsolvent recrystallization technology. The average particle (D₅₀) is 2.750 μm and 6.206 μm,impact sensitivity(H₅₀) is 35.5 cm and 34.7 cm,respectively. Thermal properties of LLM-105 were analyzed with thermogravimetry-derivative thermogravimetry（TG-DTG） and differential scanning calorimetry（DSC）. Thermal decomposition kinetics parameters of LLM-105 were obtained by Kissinger equation. The value of activation energy,pre-exponential factor and linear correlation coefficient is 257.55 kJ·mol^-1,3.3×10¹⁹ s^-1 and 0.9930,respectively.

参考文献

相似文献

引证文献

文章指标

PDF下载次数:
HTML阅读次数:
摘要点击次数:
引用次数:

引用本文

王友兵,葛忠学,王伯周,等.细颗粒LLM-105的制备及其热性能[J].含能材料, 2011, 19(5):523-526. DOI:10.3969/j. issn.1006-9941.2011.05.009.
WANG You-bing, GE Zhong-xue, WANG Bo-zhou, et al. Preparation and Thermal Properties of Fine LLM-105 with Different Crystal Form[J]. Chinese Journal of Energetic Materials, 2011, 19(5):523-526. DOI:10.3969/j. issn.1006-9941.2011.05.009.

复制

历史

收稿日期: 2010-09-08
最后修改日期: 2011-06-30
录用日期: 2011-05-31
在线发布日期: 2012-02-22
出版日期:

首页

期刊简介

编委会

作者专区

审稿专区

道德声明

联系我们

进入EMF

文章指标

引用本文

历史